Astm A276 420 Forged Round Bar 20cr13 Uns42000 Shafts Od 170mm
Astm A276 420 Forged Round Bar 20cr13 Uns42000 Shafts Od 170mm
Astm A276 420 Forged Round Bar 20cr13 Uns42000 Shafts Od 170mm
Astm A276 420 Forged Round Bar 20cr13 Uns42000 Shafts Od 170mm
Astm A276 420 Forged Round Bar 20cr13 Uns42000 Shafts Od 170mm
Astm A276 420 Soxta dumaloq novda 20cr13 Uns42000 Shaftlar Od 170mm
Xitoyning yetakchi yetkazib beruvchi va ishlab chiqaruvchisi sifatida GNEE Steel nikel asosidagi qotishma mahsulotlarni-tejamkorlik bilan ta'minlaydi.
- E-xat yuboring:ss@gneesteel.com
- Tel:+8615824687445
Qotishma 420 qotib qoladigan, martensitli zanglamaydigan po'latdir, u 410 modifikatsiyasi hisoblanadi. 410 ga o'xshab, u kamida 12% xromni o'z ichiga oladi, bu korroziyaga chidamli xususiyatlarni berish uchun etarli.
420 ning uglerod miqdori 410 ga qaraganda yuqori, bu kuch va qattiqlik xususiyatlarini optimallashtirish uchun mo'ljallangan. U tavlangan holatda yaxshi egiluvchanlikka ega, lekin 12% xrom navlarining eng yuqori qattiqligi bo'lgan Rokvell qattiqligi 50 HRC gacha qattiqlashishi mumkin. Qattiqlashuv xususiyatlariga ko'ra, 420 tez-tez payvandlanmaydi, garchi bu mumkin bo'lsa.
Martensitik zanglamaydigan po'latlar yuqori qattiqlik uchun mo'ljallangan va ba'zida boshqa xususiyatlar ma'lum darajada buziladi. Korroziyaga chidamlilik umumiy ostenitik navlarga qaraganda past va ularning foydali ishlash diapazoni noldan past haroratlarda egiluvchanlikni yo'qotishi va yuqori haroratlarda haddan tashqari issiqlik bilan kuchini yo'qotishi bilan cheklangan. Uning eng yaxshi korroziyaga chidamliligiga metall qotib qolganda va sirt silliqlanganda yoki silliqlanganda erishiladi.
ILOVALAR
420 yaxshi korroziya va ajoyib qattiqlik zarur bo'lgan turli xil ilovalar uchun ishlatiladi. Tez qattiqlashishi va korroziyaga chidamliligini yo'qotishi sababli odatda 800oF (427oC) dan yuqori haroratlarda ishlatilmaydi. 420 dan foydalanadigan ilovalarga misollar:
Kesuvchi
Pichoq pichoqlari
Jarrohlik asboblari
Ignali klapanlar
Kesish pichoqlari
Qaychi
Qo'l asboblari
| Chelik darajasi | 420 / 420F / 2Cr13 / 3Cr13 | Ilova | Yuqorida aytib o'tilgan |
| Shakl | Dumaloq bar | Standart | GB, ASTM, DIN, JIS |
| Hajmi | PH4-800 mm; uzunligi 10 m dan kam | Yuzaki | Qora, yorqin, sayqallangan, tozalangan |
| Texnika | Sovuq chizilgan; Issiq haddelenmiş; Soxtalashtirilgan | Ultrasonik test | 100% UT topshirildi |
Etkazib berish SHARTLARI
| Diametri (mm) | |
| Sovuq chizilgan | 4-60 |
| Tozalangan | 30-100 |
| Maydalangan | 4-600 |
| O'girildi | 130-800 |
| Issiq haddelenmiş | 20-280 |
| Issiq soxta | 130-800 |
ASTM 420 / 420F EKVVVALENT SARAHLARI
JIS G4303: SUS420J1/SUS420J2
ASTM/ASME: UNS S42000
EURONORM: X20Cr13/ X30Cr13
DIN: 1.4021/1.4028
KIMYOVIY TARKIBI (%)
| C | Si | Mn | P | S | Cr | |
| 420 |
dan kichik yoki teng 0.15 |
dan kichik yoki teng 1.00 |
dan kichik yoki teng 1.00 |
dan kichik yoki teng 0.040 |
dan kichik yoki teng 0.030 |
12.00 14.00 |
| 2Cr13 |
0.16 0.25 |
dan kichik yoki teng 1.00 |
dan kichik yoki teng 1.00 |
dan kichik yoki teng 0.040 |
dan kichik yoki teng 0.030 |
12.00 14.00 |
| 3Cr13 |
0.26 0.35 |
dan kichik yoki teng 1.00 |
dan kichik yoki teng 1.00 |
dan kichik yoki teng 0.040 |
dan kichik yoki teng 0.030 |
12.00 14.00 |
MEXANIK XUSUSIYATLARI
| Temperatsiya harorati | Kuchlanish kuchi ksi (min) | Hosildorlik kuchi 0.2% ksi (min) | Uzayish % | Qattiqlik (Brinell) MAX |
| Tavlangan | 655 | 345 | 25 | 214 maks |
| 399 daraja F (204 daraja) | 1600 | 1360 | 12 | 444 |
| 600 daraja F (316 daraja) | 1580 | 1365 | 14 | 444 |
| 800 daraja F (427 daraja) | 1620 | 1420 | 10 | 461 |
| 1000 daraja F (538 daraja) | 1305 | 1095 | 15 | 375 |
| 1099 daraja F (593 daraja) | 1035 | 810 | 18 | 302 |
| 1202 daraja F (650 daraja) | 895 | 680 | 20 | 262 |
| Baho | Kuchlanish kuchi ksi (min) | Hosildorlik kuchi 0.2% ksi (min) | Uzayish % | Qattiqlik (Brinell) MAX |
| 2Cr13% 2f20Cr13 | 640 | 440 | 20 | 223 |
| 3Cr13% 2f30Cr13 | 735 | 540 | 12 | 235 |
QARShILISH
Korroziyaga qarshilik:
Ostenitik navlarga va 17% xrom ferritik qotishmalariga qaraganda kamroq chidamli
Qattiqlashtirilgan holatda atmosferaga, oziq-ovqatlarga, toza suvga va engil kislotalarga yaxshi qarshilik
Tavlangan holatda qarshilik pasaygan
Eng yaxshisi silliq sirt qoplamasi bilan
Issiqlik qarshiligi:
Mexanik xususiyatlar pasayganligi sababli, tegishli temperleme haroratidan yuqori foydalanish tavsiya etilmaydi
O'lchov harorati taxminan 1202oF (650oC)
QAYTA QILISH
Ishlov berish qobiliyati
Qattiq, ipli chip hosil bo'lishi.
Ba'zi yuqori uglerodli asbob po'latlarini qayta ishlashga o'xshaydi
Payvandlash
Havoning qattiqlashuvi xususiyatlari tufayli odatda payvandlanmaydi.
Payvandlash 300-400 F ga oldindan qizdirilgandan keyin amalga oshirilishi mumkin
2 soat davomida haroratda payvandlangandan keyin temperatura
Issiq ishlash
Haroratni asta-sekin 1400 darajaga, keyin esa 2000-2200 F ga oshirish tavsiya etiladi
Pechni ishlagandan so'ng, yorilib ketmaslik uchun sekin soviydi
Ish haroratini 1600 F dan yuqori ushlab turish uchun qayta isitish kerak.
Sovuq ishlash
Faqat kichik sovuq ishlarga bardosh bera oladi.
Radikal shakllantirish operatsiyalari yorilishga olib keladi.
Yuvish
1550-1650 F (843-900 C) gacha bo'lgan haroratlarda tavlanadi
Pechni sekin sovutishga ruxsat bering.
Temperlash
300-400 F haroratda harorat
Maksimal qattiqlik va korroziyaga chidamlilik uchun havo sovutadi.
Qattiqlashuv
Qizdirilgan yog'da o'chirish uchun 1850-1950 F haroratda namlang.